METAL REPAIR Compound Rocol 56g RS64012

METAL REPAIR Compound Rocol

METAL REPAIR Compound is a steel reinforced epoxy putty with non-rusting metallic fillers, designed for use as a fast, solvent-free, permanent repair compound for items manufactured from ferrous metals, aluminium and other metallic substrates. Simple and convenient to use, it bonds to a wide range of substrates, including metal, glass, ceramic, concrete, fibreglass and wood, and is perfect for filling cracks and holes. It eliminates the need for welding and brazing, and can be applied underwater. METAL REPAIR Compound is not intended for structural repair. The formula is resistant to hydrocarbons, ketones, alcohols, esters, halocarbons, aqueous salt solutions, dilute acids and caustics, and is suitable tor continuous use in temperatures up to +120ºC (+150ºC for intermittent use). The compound holds in 4-10 minutes and is usable after 1 hour, with a full cure after 24 hours.

Application: Repairing castings, valve and pump components, shafts, keyways, bearings, pipes, flanges, tanks, housings and any cracked, broken or worn equipment.

Technical data:
Base type: epoxy resin
Solids: non-rusting metallic fillers
Shore D hardness: 80
Compressive strength: 80N/mm2
Dielectric strength: 300V/mm
Electrical resistance: 30,000MΩ
Lap shear strength on steel: 6.2N/mm2
Volume fill per 56g stick: approx. 34cm3
Working life: 3min at 20ºC
Initial set: 4-10min
Usable strength: 60min at 20ºC
Full cure: 24h at 20ºC
Temperature range during application: +4ºC - +43ºC
Temperature range when cured: -40ºC - +120ºC continuously; -40ºC - +150ºC for intermittent use
Storage temperature: +8ºC - +28ºC
Shelf life: 1 year